MATERIAL DESIGNATION:GBT 022Cr24Ni17Mo5Mn6NbN
| Standard: |
GBT |
| Country: |
China |
| Application: |
|
| Recommend a supplier |
| Company name: |
Haihong International Trade (HK) CO., Limited; |
| Production range: |
- 022Cr24Ni17Mo5Mn6NbN round bar, Dimension: 0.1mm to 4000mm
- 022Cr24Ni17Mo5Mn6NbN square bar, Dimension: 8mm to 4000mm
- 022Cr24Ni17Mo5Mn6NbN plate,sheet,flat,coil,strip, Dimension: 0.08mm to 2000mm(THK)*2mm to 4000mm(width)*Lenght(According to the demand for custom)
- 022Cr24Ni17Mo5Mn6NbN forged, stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
- Delivery: hot forging or hot rolling and annealing or normalizing + tempering/quenching + tempering any other conditions based on the customer's requirement
|
| Telephone: |
+86-816-3653300 |
| Fax: |
+86-816-3639422 |
| E-mail: |
E-mail:sales@x65cr13.com |
| Contact: |
Mr. Chen |
Chemical Composition (%)
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | W(%) | N(%) | Nb(%) |
| 0.03 | 1.0 | 5.0-7.0 | 0.03 | 0.01 | 23.0-25.0 | 16.0-18.0 | 4.0-5.0 | 2.0-2.5 | 0.4-0.6 | 0.1 |
Mechanical Properties
| |
Min. |
Max. |
Approx |
| Castings; Homogenization, Solution and Precipitation Heat Treated (H1100); separately cast test pieces |
| Yield stress Rp0,2 (MPa) |
827 |
- |
- |
| Tensile stress, Rm (MPa) |
896 |
- |
- |
| Elongation, A (%) |
10.0 |
- |
- |
| Elongation in 4 x Diameter % |
| Impact, Kv/Ku (J) |
- |
- |
- |
| Hardness |
| HR min |
HR max |
|
| 30 |
38 |
|
| HRC |
| Castings; Homogenization, Solution and Precipitation Heat Treated (H1100); Integrally cast specimens |
| Yield stress Rp0,2 (MPa) |
827 |
- |
- |
| Tensile stress, Rm (MPa) |
896 |
- |
- |
| Elongation, A (%) |
6.0 |
- |
- |
| Elongation in 4 x Diameter % |
| Impact, Kv/Ku (J) |
- |
- |
- |
| Hardness |
| HR min |
HR max |
|
| 30 |
38 |
|
| HRC |
This standard specifies the stainless steel rods order contents, classification, code, size, shape, weight and allowable deviation, technical requirements, test methods, inspection rules, packaging, logo and certificate of quality.This standard applies to the size is not more than 250 mm hot rolled and forged stainless steel rods.The supply and demand both sides talks things over, can also supply the size larger than 250 mm hot rolled and forged stainless steel rods.