MATERIAL DESIGNATION:ASTM ASTM A182 F55
| Standard: |
ASTM |
| Country: |
USA |
| Application: |
|
| Recommend a supplier |
| Company name: |
Haihong International Trade (HK) CO., Limited; |
| Production range: |
- ASTM A182 F55 round bar, Dimension: 0.1mm to 4000mm
- ASTM A182 F55 square bar, Dimension: 8mm to 4000mm
- ASTM A182 F55 plate,sheet,flat,coil,strip, Dimension: 0.08mm to 2000mm(THK)*2mm to 4000mm(width)*Lenght(According to the demand for custom)
- ASTM A182 F55 forged, stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
- Delivery: hot forging or hot rolling and annealing or normalizing + tempering/quenching + tempering any other conditions based on the customer's requirement
|
| Telephone: |
+86-816-3653300 |
| Fax: |
+86-816-3639422 |
| E-mail: |
E-mail:sales@x65cr13.com |
| Contact: |
Mr. Chen |
Chemical Composition (%)
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | W(%) | N(%) | Cu(%) |
| ≤0.03 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.015 | 24.00~26.00 | 6.00~8.00 | 3.00~4.00 | 0.50~1.00 | 0.20~0.30 | 0.50~1.00 |
Mechanical Properties
| |
Min. |
Max. |
Approx |
| Castings; Homogenization, Solution and Precipitation Heat Treated (H1100); separately cast test pieces |
| Yield stress Rp0,2 (MPa) |
827 |
- |
- |
| Tensile stress, Rm (MPa) |
896 |
- |
- |
| Elongation, A (%) |
10.0 |
- |
- |
| Elongation in 4 x Diameter % |
| Impact, Kv/Ku (J) |
- |
- |
- |
| Hardness |
| HR min |
HR max |
|
| 30 |
38 |
|
| HRC |
| Castings; Homogenization, Solution and Precipitation Heat Treated (H1100); Integrally cast specimens |
| Yield stress Rp0,2 (MPa) |
827 |
- |
- |
| Tensile stress, Rm (MPa) |
896 |
- |
- |
| Elongation, A (%) |
6.0 |
- |
- |
| Elongation in 4 x Diameter % |
| Impact, Kv/Ku (J) |
- |
- |
- |
| Hardness |
| HR min |
HR max |
|
| 30 |
38 |
|
| HRC |
Minimum Mechanical Properties at Room Temperature
(EN10088-3 1.4501 UNS S32760 F55 160mm dia max - solution treated)
| Tensile (UTS) |
|
730 - 930 N/mm² |
| 0.2% Proof Stress |
|
530 N/mm² Min |
| Elongation |
|
25% min |
| Hardness |
|
290HB Max |
| Impact |
|
100J |