MATERIAL DESIGNATION: W18Cr4V
| Standard: |
|
| Country: |
China |
| Application: |
|
| Recommend a supplier |
| Company name: |
Haihong International Trade (HK) CO., Limited; |
| Production range: |
- W18Cr4V round bar, Dimension: 0.1mm to 4000mm
- W18Cr4V square bar, Dimension: 8mm to 4000mm
- W18Cr4V plate,sheet,flat,coil,strip, Dimension: 0.08mm to 2000mm(THK)*2mm to 4000mm(width)*Lenght(According to the demand for custom)
- W18Cr4V forged, stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
- Delivery: hot forging or hot rolling and annealing or normalizing + tempering/quenching + tempering any other conditions based on the customer's requirement
|
| Telephone: |
+86-816-3653300 |
| Fax: |
+86-816-3639422 |
| E-mail: |
E-mail:sales@x65cr13.com |
| Contact: |
Mr. Chen |
Chemical Composition (%)
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | V(%) | W(%) | Cu(%) |
| 0.70～0.80 | 0.20～0.40 | 0.10～0.40 | ≤0.030 | ≤0.030 | 3.80～4.40 | ≤0.30 | ＜0.30(4) | 1.00～1.40 | 17.5～19.00 | ≤0.25 |
Mechanical Properties
| |
Min. |
Max. |
Approx |
| Castings; Homogenization, Solution and Precipitation Heat Treated (H1100); separately cast test pieces |
| Yield stress Rp0,2 (MPa) |
827 |
- |
- |
| Tensile stress, Rm (MPa) |
896 |
- |
- |
| Elongation, A (%) |
10.0 |
- |
- |
| Elongation in 4 x Diameter % |
| Impact, Kv/Ku (J) |
- |
- |
- |
| Hardness |
| HR min |
HR max |
|
| 30 |
38 |
|
| HRC |
| Castings; Homogenization, Solution and Precipitation Heat Treated (H1100); Integrally cast specimens |
| Yield stress Rp0,2 (MPa) |
827 |
- |
- |
| Tensile stress, Rm (MPa) |
896 |
- |
- |
| Elongation, A (%) |
6.0 |
- |
- |
| Elongation in 4 x Diameter % |
| Impact, Kv/Ku (J) |
- |
- |
- |
| Hardness |
| HR min |
HR max |
|
| 30 |
38 |
|
| HRC |
The performance characteristics of high-speed tool steel with purpose
(1) use of steel DianZhaLu smelting, the silicon content not specified limit.
(2) in order to improve steel cutting machining, the buyer's request, can be provisions for sulfur ω (S) 0.60% ~ 0.15%.
(3) of residual elements in steel (mass fraction) : 0.30% or Ni; Cu 0.25% or less.
(4) is the high tungsten molybdenum content allowed ω (Mo) more than 1.00%. Steel tungsten molybdenum and the relationship is: when molybdenum content more than ω (Mo) 0.30%, tungsten content reduced correspondingly, in molybdenum content more than ω (Mo) 0.30% of the part, each ω (Mo) 1% can replace ω (W) 2%, if meet this kind of case, in this GangHao add after "Mo".
(5) W6Mo5Cr4V2 steel according to both the supply and the demand agreement, adjust the content of vanadium ω (V) 1.60% ~ 2.20%.